| 铸锭规格/mm | 性能 |
均火温度 | |||||||
| 400℃ | 420℃ | 440℃ | 460℃ | 470℃ | 475℃ | 480℃ | 500℃ | ||
| φ172 |
σ0.2/MPa |
308.7 | 316.5 | 352.8 | 355.7 | 348.9 | 359.7 | 354.8 | 342.0 |
| σb/MPa | 315.6 | 335.2 | 388.1 | 425.3 | 427.3 | 426.3 | 415.5 | 295.0 | |
| δ/% | 4.1 | 4.7 | 4.8 | 9.2 | 9.3 | 9.5 | 10.0 | 7.3 | |
| φ200 | σ0.2/MPa | 304.8 | 322.4 | 341.0 | 352.8 | 356.7 | 357.7 | 357.7 | 352.3 |
| σb/MPa | 304.4 | 323.4 | 342.0 | 372.4 | 378.3 | 375.3 | 373.4 | 364.6 | |
| δ/% | 0.7 | 0.8 | 1.3 | 2.0 | 2.5 | 3.3 | 3.5 | 3.3 | |
| φ300 | σ0.2/MPa | 308.7 | 307.7 | 340.1 | 351.8 | 356.3 | 355.7 | 365.5 | 344.9 |
| σb/MPa | 307.7 | 308.7 | 345.7 | 353.7 | 363.7 | 373.4 | 370.4 | 346.9 | |
| δ/% | 1.3 | 1.2 | 1.5 | 2.7 | 3.5 | 3.5 | 4 | 2.7 | |
| φ420 | σ0.2/MPa | 225.4 | 266.6 | 294.9 | 294.8 | 340.9 | 343.0 | 338.9 | 320.5 |
| σb/MPa | 225.9 | 267.6 | 296.0 | 303.8 | 342.9 | 343.0 | 340.2 | 323.5 | |
| δ/% | 2.3 | 2.2 | 2.7 | 2.7 | 3.7 | 3.8 | 4.0 | 3.3 | |
7A04合金不同均火温度铸锭的力学
来源：中国铝材信息网
发布时间：2006/11/22 16:02:09